This full fuse firing was all about testing a few ideas to make glass cabochons for jewellery. You will notice in the ‘Before’ photo that the items are placed on separate pieces of BullsEye Thinfire kiln shelf paper. For no specific reason other than to use up the paper offcuts.
All glass is BullsEye COE 90. Most glass is 3mm, but there were a few 2mm pieces in some stacks. Everything was fired to a full fuse. The Firing Schedule I used is shown below.
Continue reading Test Cabochons and More
This was my first attempt at a fused glass clock face, but it was a bit of a disaster from the beginning. However, there are a few lessons to be learnt here.
First one is to take better photos. The one and only photo I have is by my iPhone and it isn’t great, but you should get the idea. Taking photos is a fantastic way of documenting your efforts, successes and failures. Combine this with details of the design, materials used, firing schedule and results and you have a great log for future reference. I just have to follow my own advice:)
The concept was a black and white clock face with a city skyline in silhouette. The black and white I felt would give a nice clean and simple feel that could fit into any décor.
Continue reading First Attempt at a Fused Glass Clock
This was a milestone – my very first glass fuse firing.
What’s a glass puddle? Well, I didn’t have the faintest when I first heard the term. It is basically a technique for creating jewellery cabochons.
The idea is to layer up a number of pieces of art glass in complimenting colours, then full fuse that together into a puddle. The glass completely fuses down and melts together into what is literally a puddle of glass.
You then break that up, and that is a challenge, into small pieces, set them on edge and again fire to a full fuse. Other than deciding what colour glass to use and how to layer it up, there is not a lot of control over the final result. I suppose it was this that attracted me to the idea; the mystery of the final result.
Continue reading First Glass Fusing for a Puddle
This is the first post of what I expect to be many about the evolution of our studio. We are learning so we do expect to be making changes to the studio as we discover what does and does not work for us.
Having said that, we love our studio. It is our new playground and where we spend quite a lot of time here.
You can see we have a dedicated area for cutting and working with glass, another where Ann works with her creations and the kiln is in a separate area, well away from combustible items.
Continue reading Our Studio
This was actually a bigger problem than I expected.
We needed a good sized workbench that was very solid and sturdy, and at the right height. The sizes was important because we needed enough room to have the cutting station but also area for project setup, kiln shelf preparation, general design work and what ever else came up. Room in the studio wasn’t a real big issue, but we had to consider future improvements and decided not take up too much space.
Continue reading Our Budget Workbench
Not sure if anybody is really interested, but thought I would post a little about building our studio. By the way, please excuse the photos. They were taken with an old iPhone.
The studio is for working with glass, as in glass fusing, glass slumping and glass draping. It is also a work area for Ann working with silver, copper and other metals. She has another area in the house for more assembly work to do with jewellery and other crafts.
Continue reading Building our Studio